| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.57to1.61 |
g/cm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
抗张强度 |
0.381mm |
ASTMD412 |
17.9 |
MPa |
| ELASTOMERS |
抗张强度 |
1.91mm |
ASTMD412 |
15.9 |
MPa |
| ELASTOMERS |
伸长率 |
Break,1.91mm |
ASTMD412 |
210 |
% |
| ELASTOMERS |
伸长率 |
Break,0.381mm |
ASTMD412 |
190 |
% |
| 硬度 |
肖氏硬度 |
邵氏D |
ASTMD2240 |
67to73 |
|
| 硬度 |
肖氏硬度 |
邵氏D,15秒 |
ASTMD2240 |
54to60 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-4.00 |
°C |
| 老化 |
ChangeinTensileStrengthinAir2(100°C,240hr) |
|
ULUnspecified |
-1.0 |
% |
| 老化 |
ChangeinUltimateElongationinAir2(100°C,240hr) |
|
ULUnspecified |
-7.0 |
% |
| 电气性能 |
DielectricConstant(23°C,100MHz) |
|
ASTMD150 |
3.35 |
|
| 电气性能 |
DissipationFactor(23°C,100MHz) |
|
ASTMD150 |
0.014 |
|
| 可燃性 |
极限氧指数(3.18mm) |
|
ASTMD2863 |
51 |
% |