| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.931 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
|
ASTMD1238 |
0.55 |
g/10min |
| 物理性能 |
醋酸乙烯含量 |
|
|
4.0 |
wt% |
| 机械性能 |
摩擦系数(吹塑薄膜) |
|
ASTMD1894 |
0.50 |
|
| 薄膜 |
薄膜厚度-经测试 |
|
|
38 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD2(38µm,BlownFilm) |
|
ASTMD882 |
166 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD2(38µm,BlownFilm) |
|
ASTMD882 |
200 |
MPa |
| 薄膜 |
TensileStrength-MD2(Break,38µm,BlownFilm) |
|
ASTMD882 |
22.0 |
MPa |
| 薄膜 |
TensileStrength-TD2(Break,38µm,BlownFilm) |
|
ASTMD882 |
17.0 |
MPa |
| 薄膜 |
TensileElongation-MD2(Break,38µm,BlownFilm) |
|
ASTMD882 |
230 |
% |
| 薄膜 |
TensileElongation-TD2(Break,38µm,BlownFilm) |
|
ASTMD882 |
600 |
% |
| 薄膜 |
落锤冲击2(38µm,吹塑薄膜) |
|
ASTMD1709 |
160 |
g |
| 光学性能 |
光泽度(45°,38.0µm,吹塑薄膜) |
|
ASTMD2457 |
50 |
|
| 光学性能 |
Haze(38.1µm,BlownFilm) |
|
ASTMD1003 |
13 |
% |