| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.933 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
|
ASTMD1238 |
2.5 |
g/10min |
| 物理性能 |
醋酸乙烯含量 |
|
|
12.0 |
wt% |
| 薄膜 |
薄膜厚度-经测试 |
|
|
33 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD2(33µm,BlownFilm) |
|
ASTMD882 |
72.4 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD2(33µm,BlownFilm) |
|
ASTMD882 |
79.3 |
MPa |
| 薄膜 |
TensileStrength-MD2(Break,33µm,BlownFilm) |
|
ASTMD882 |
26.9 |
MPa |
| 薄膜 |
TensileStrength-TD2(Break,33µm,BlownFilm) |
|
ASTMD882 |
22.1 |
MPa |
| 薄膜 |
TensileElongation-MD2(Break,33µm,BlownFilm) |
|
ASTMD882 |
300 |
% |
| 薄膜 |
TensileElongation-TD2(Break,33µm,BlownFilm) |
|
ASTMD882 |
800 |
% |
| 薄膜 |
落锤冲击2(32µm,吹塑薄膜) |
|
ASTMD1709 |
240 |
g |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
70.0 |
°C |
| 热性能 |
熔融峰值温度 |
|
ASTMD3418 |
94.0 |
°C |
| 光学性能 |
Gloss(45°,33.0µm,BlownFilm) |
|
ASTMD2457 |
84 |
|
| 光学性能 |
Haze(33.0µm,BlownFilm) |
|
ASTMD1003 |
2.3 |
% |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
BlownFilmMeltTemperature |
|
|
<193 |
°C |
| ADDITIONAL INFORMATION |
CastFilmMeltTemperature |
|
|
<210 |
°C |