| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.934 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.55 |
g/10min |
| 物理性能 |
醋酸乙烯含量 |
|
|
12.5 |
wt% |
| 薄膜 |
薄膜厚度-经测试 |
|
|
51 |
µm |
| 薄膜 |
割线模量-1%正割,MD(51µm,吹塑薄膜) |
|
ASTMD882 |
75.8 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(51µm,BlownFilm) |
|
ASTMD882 |
89.6 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,51µm,BlownFilm) |
|
ASTMD882 |
27.6 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,51µm,BlownFilm) |
|
ASTMD882 |
29.6 |
MPa |
| 薄膜 |
伸长率-MD(断裂,51µm,吹塑薄膜) |
|
ASTMD882 |
450 |
% |
| 薄膜 |
TensileElongation-TD(Break,51µm,BlownFilm) |
|
ASTMD882 |
950 |
% |
| 薄膜 |
DartDropImpact(51µm,BlownFilm) |
|
ASTMD1709 |
580 |
g |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
76.0 |
°C |
| 热性能 |
熔融峰值温度 |
|
ASTMD3418 |
94.0 |
°C |
| 光学性能 |
Gloss(45°,50.8µm,BlownFilm) |
|
ASTMD2457 |
70 |
|
| 光学性能 |
雾度(50.8µm,吹塑薄膜) |
|
ASTMD1003 |
4.0 |
% |