| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.930 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
2.0 |
g/10min |
| 物理性能 |
醋酸乙烯含量 |
|
|
9.0 |
wt% |
| 薄膜 |
薄膜厚度-经测试 |
|
|
38 |
µm |
| 薄膜 |
TensileStrength-MD(Break,38µm) |
|
ASTMD882 |
31.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,38µm) |
|
ASTMD882 |
27.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,38µm) |
|
ASTMD882 |
330 |
% |
| 薄膜 |
TensileElongation-TD(Break,38µm) |
|
ASTMD882 |
650 |
% |
| 薄膜 |
落锤冲击2(38µm) |
|
ASTMD1709 |
250 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(38µm) |
|
ASTMD1922 |
120 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(38µm) |
|
ASTMD1922 |
100 |
g |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
81.0 |
°C |
| 热性能 |
熔融温度 |
|
DSC |
99.0 |
°C |
| 光学性能 |
Haze(38.0µm) |
|
ASTMD1003 |
1.5 |
% |