| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.935 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.50 |
g/10min |
| 物理性能 |
醋酸乙烯含量 |
|
|
13.5 |
wt% |
| 机械性能 |
抗张强度(断裂,模压成型) |
|
ASTMD638 |
25.0 |
MPa |
| 机械性能 |
伸长率(断裂,模压成型) |
|
ASTMD638 |
680 |
% |
| 薄膜 |
SecantModulus-2%Secant,MD(50µm,BlownFilm) |
|
ASTMD882 |
60.0 |
MPa |
| 薄膜 |
SecantModulus-2%Secant,TD(50µm,BlownFilm) |
|
ASTMD882 |
70.0 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,50µm,BlownFilm) |
|
ASTMD882 |
32.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,50µm,BlownFilm) |
|
ASTMD882 |
32.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,50µm,BlownFilm) |
|
ASTMD882 |
750 |
% |
| 薄膜 |
TensileElongation-TD(Break,50µm,BlownFilm) |
|
ASTMD882 |
800 |
% |
| 薄膜 |
落锤冲击(50µm,吹塑薄膜) |
|
ASTMD1709B |
730 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(50µm,BlownFilm) |
|
ASTMD1922 |
240 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(50µm,BlownFilm) |
|
ASTMD1922 |
350 |
g |
| 硬度 |
肖氏硬度 |
邵氏A,模压成型 |
ASTMD2240 |
91 |
|
| 硬度 |
肖氏硬度 |
邵氏D,模压成型 |
ASTMD2240 |
50 |
|
| 热性能 |
维卡软化温度 |
|
ASTMD15252 |
75.0 |
°C |
| 热性能 |
熔融峰值温度 |
|
ASTMD3418 |
94.0 |
°C |
| 光学性能 |
光泽度(45°,50.0µm,吹塑薄膜) |
|
ASTMD2457 |
95 |
|
| 光学性能 |
雾度(50.0µm,吹塑薄膜) |
|
ASTMD1003 |
2.0 |
% |