| 规格级别 | 阻燃 其它 挤出 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 低（至无）铅含量，阻燃性能 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
|
物理性能
|
比重 | ASTM D792 | 1.48 到 1.52 | g/cm³ | |
| 硬度计硬度 | 支撐 A | ASTM D2240 | 96 | ||
| 支撐 A, 15 秒 | ASTM D2240 | 92 | |||
| 支撐 D | ASTM D2240 | 58 | |||
| 支撐 D, 15 秒 | ASTM D2240 | 42 | |||
|
机械性能
|
抗张强度 | 屈服, 0.381 mm | ASTM D412 | 17.2 | MPa |
| 屈服, 0.610 mm | ASTM D412 | 15.9 | MPa | ||
| 屈服, 1.91 mm | ASTM D412 | 14.5 | MPa | ||
| 断裂 2 | ASTM D412 | 250 | % | ||
| 伸长率 | 断裂 3 | ASTM D412 | 280 | % | |
| 断裂 4 | ASTM D412 | 230 | % | ||
| 老化 |
空气中拉伸强度的变化率 5 | 100°C, 168 hr | ASTM D573 | 0.0 | % |
| 100°C, 240 hr | ASTM D573 | 5.0 | % | ||
| 113°C, 168 hr | ASTM D573 | 8.0 | % | ||
| 空气中极限伸长率的变化率 5 | 38°C, 168 hr | ASTM D573 | -15 | % | |
| 100°C, 240 hr | ASTM D573 | -17 | % | ||
| 113°C, 168 hr | ASTM D573 | -38 | % | ||
| 热性能 | 脆化温度 | ASTM D746 | -15.0 | ℃ | |
| 电气性能 | 介电常数 | 23℃, 100 MHz | ASTM D150 | 3.30 | |
| 耗散因数 | 23℃, 100 MHz | ASTM D150 | 0.026 | ||
| 可燃性 | 极限氧指数 | 3.18 mm | ASTM D2863 | 39 | % |
| 挤出 | 第1气缸区温度 | 154 | ℃ | ||
| 第2气缸区温度 | 160 | ℃ | |||
| 第3气缸区温度 | 166 | ℃ | |||
| 第4气缸区温度 | 168 | ℃ | |||
| 第5气缸区温度 | 171 | ℃ | |||
| 连接器温度 | 177 | ℃ | |||
| 熔体温度 | 171到 182 | ℃ | |||
| 模具温度 | 177 | ℃ | |||