| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.942 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
2.1 |
g/10min |
| 物理性能 |
甲基丙烯酸含量 |
|
|
17.0 |
wt% |
| 机械性能 |
抗张强度2(断裂) |
|
ASTMD638 |
12.0 |
MPa |
| 机械性能 |
伸长率2(断裂) |
|
ASTMD638 |
730 |
% |
| 薄膜 |
SecantModulus-1%Secant,MD(38µm,BlownFilm) |
|
ASTMD882 |
52.0 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(38µm,BlownFilm) |
|
ASTMD882 |
62.0 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,38µm,BlownFilm) |
|
ASTMD882 |
22.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,38µm,BlownFilm) |
|
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,38µm,BlownFilm) |
|
ASTMD882 |
470 |
% |
| 薄膜 |
TensileElongation-TD(Break,38µm,BlownFilm) |
|
ASTMD882 |
720 |
% |
| 薄膜 |
落锤冲击(38µm,吹塑薄膜) |
|
ASTMD1709A |
300 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(38µm,BlownFilm) |
|
ASTMD1922 |
70 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-TD(38µm,吹塑薄膜) |
|
ASTMD1922 |
400 |
g |
| 薄膜 |
始封温度 |
|
|
68.0 |
°C |
| 硬度 |
肖氏硬度(邵氏D) |
|
ASTMD2240 |
37 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
<-73.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
60.0 |
°C |
| 热性能 |
熔融峰值温度 |
|
ASTMD3418 |
82.0 |
°C |
| 光学性能 |
光泽度(45°,38.0µm,吹塑薄膜) |
|
ASTMD2457 |
15 |
|
| 光学性能 |
Haze(38.1µm,BlownFilm) |
|
ASTMD1003 |
53 |
% |