| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792B |
0.900 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
6.5 |
g/10min |
| 机械性能 |
抗张强度(屈服) |
|
ASTMD638 |
27.6 |
MPa |
| 机械性能 |
伸长率(屈服) |
|
ASTMD638 |
13 |
% |
| 机械性能 |
弯曲模量-1%正割2 |
|
ASTMD790A |
896 |
MPa |
| 机械性能 |
摩擦系数 |
|
ASTMD1894 |
0.15to0.25 |
|
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
割线模量-1%正割,MD(25µm) |
|
ASTMD882 |
655 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(25µm) |
|
ASTMD882 |
621 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,25µm) |
|
ASTMD882 |
49.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,25µm) |
|
ASTMD882 |
32.4 |
MPa |
| 薄膜 |
伸长率-MD(断裂,25µm) |
|
ASTMD882 |
730 |
% |
| 薄膜 |
TensileElongation-TD(Break,25µm) |
|
ASTMD882 |
710 |
% |
| 薄膜 |
落锤冲击 |
0°C,25µm |
ASTMD1709 |
360 |
g |
| 薄膜 |
落锤冲击 |
23°C,25µm |
ASTMD1709 |
1900 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD(25µm) |
|
ASTMD1922 |
25 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(25µm) |
|
ASTMD1922 |
500 |
g |
| 薄膜 |
SealInitiationTemperature(25µm) |
|
|
135 |
°C |
| 薄膜 |
DartDropTest |
0°C,25.0µm |
ASTMD1709 |
35.6 |
J/cm |
| 薄膜 |
DartDropTest |
23°C,25.0µm |
ASTMD1709 |
187 |
J/cm |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C) |
|
ASTMD256A |
69 |
J/m |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
76.1 |
°C |
| 光学性能 |
光泽度(45°,25.0µm) |
|
ASTMD2457 |
80to85 |
|
| 光学性能 |
雾度(25.0µm) |
|
ASTMD1003 |
3.0 |
% |