| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.910 |
g/cm³ |
| 物理性能 |
密度 |
|
ISO1183 |
0.910 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
35 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ISO1133 |
35 |
g/10min |
| 机械性能 |
TensileModulus(0.0250mm) |
|
ASTMD638 |
650 |
MPa |
| 机械性能 |
TensileModulus(0.0250mm) |
|
ISO527-2 |
650 |
MPa |
| 机械性能 |
TensileStrength(Yield,0.0250mm) |
|
ASTMD638 |
22.0 |
MPa |
| 机械性能 |
TensileStress(Yield,0.0250mm) |
|
ISO527-2 |
22.0 |
MPa |
| 机械性能 |
TensileElongation(Break,0.0250mm) |
|
ASTMD638 |
>500 |
% |
| 机械性能 |
TensileStrain(Break,0.0250mm) |
|
ISO527-2 |
>500 |
% |
| 热性能 |
维卡软化温度 |
|
ASTMD15252 |
138 |
°C |
| 热性能 |
维卡软化温度 |
|
ISO306/A |
138 |
°C |
| 热性能 |
熔融温度 |
|
ISO11357-3 |
160 |
°C |