| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.938 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
20 |
g/10min |
| 物理性能 |
MoldingShrinkage-Flow(23°C,3.18mm) |
|
InternalMethod |
0.16to0.22 |
% |
| 机械性能 |
抗张强度(屈服,23°C,3.18mm) |
|
ASTMD638 |
16.5 |
MPa |
| 机械性能 |
TensileElongation(Yield,23°C,3.18mm) |
|
ASTMD638 |
8.0 |
% |
| 机械性能 |
弯曲模量-正切(23°C,3.18mm) |
|
ASTMD790 |
758 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,3.18mm) |
|
ASTMD256 |
NoBreak |
|
| 冲击性能 |
GardnerImpact(23°C,3.18mm) |
|
ASTMD5420 |
18.1 |
J |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火,3.18mm) |
|
ASTMD648 |
79.4 |
°C |
| 热性能 |
RTIElec(1.5mm) |
|
UL746 |
115 |
°C |
| 热性能 |
RTIImp(1.5mm) |
|
UL746 |
115 |
°C |
| 热性能 |
RTIStr(1.5mm) |
|
UL746 |
115 |
°C |
| 可燃性 |
UL阻燃等级(1.5mm) |
|
UL94 |
V-2 |
|