| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.07 |
g/cm³ |
| 物理性能 |
MeltMass-FlowRate(MFR)2(220°C/10.0kg) |
|
ASTMD1238 |
20 |
g/10min |
| 物理性能 |
收缩率-流动 |
|
ASTMD955 |
0.40to0.80 |
% |
| 机械性能 |
TensileModulus-Tangent3(23°C,InjectionMolded) |
|
ASTMD638 |
2570 |
MPa |
| 机械性能 |
TensileStrength3(Yield,23°C,InjectionMolded) |
|
ASTMD638 |
45.9 |
MPa |
| 机械性能 |
TensileElongation3(Yield,23°C,InjectionMolded) |
|
ASTMD638 |
2.9 |
% |
| 机械性能 |
FlexuralModulus-Tangent4(3.18mm,50.8mmSpan) |
|
ASTMD790 |
2500 |
MPa |
| 机械性能 |
FlexuralStrength4(Yield,23°C,3.18mm,InjectionMolded,50.8mmSpan) |
|
ASTMD790 |
75.8 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,3.18mm) |
|
ASTMD256 |
120 |
J/m |
| 热性能 |
DeflectionTemperatureUnderLoad(1.8MPa,Unannealed,3.18mm,InjectionMolded) |
|
ASTMD648 |
78.9 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15255 |
106 |
°C |