| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.902 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
5.0 |
g/10min |
| 机械性能 |
抗张强度2(屈服) |
|
ASTMD638 |
23.9 |
MPa |
| 机械性能 |
抗张强度2(断裂) |
|
ASTMD638 |
14.1 |
MPa |
| 机械性能 |
伸长率2(屈服) |
|
ASTMD638 |
6.6 |
% |
| 机械性能 |
伸长率2(断裂) |
|
ASTMD638 |
280 |
% |
| 机械性能 |
弯曲模量-1%正割 |
|
ASTMD790A |
1230 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(-20°C) |
|
ASTMD256 |
80 |
J/m |
| 冲击性能 |
NotchedIzodImpact(Area) |
-20°C |
ASTMD256 |
7.80 |
kJ/m² |
| 冲击性能 |
NotchedIzodImpact(Area) |
23°C |
ASTMD256 |
NoBreak |
|
| 冲击性能 |
InstrumentedImpact,Ductility |
-20°C |
ASTMD3763 |
Ductile |
|
| 冲击性能 |
InstrumentedImpact,Ductility |
23°C |
ASTMD3763 |
Ductile |
|
| 硬度 |
洛氏硬度(R级) |
|
ASTMD785 |
79 |
|
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
95.0 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火) |
|
ASTMD648 |
48.9 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
149 |
°C |
| 热性能 |
RTIElec(1.5mm) |
|
UL746 |
65.0 |
°C |
| 热性能 |
RTIImp(1.5mm) |
|
UL746 |
65.0 |
°C |
| 热性能 |
RTIStr(1.5mm) |
|
UL746 |
65.0 |
°C |
| 可燃性 |
UL阻燃等级(1.5mm) |
|
UL94 |
HB |
|
| 光学性能 |
光泽度(60°) |
|
ASTMD2457 |
60 |
|