PP | HI5204B
生产厂家：LG化学
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D-792 |
0.99 |
|
| 成型收缩率 |
|
ASTM D-955 |
1.2-1.4 |
% |
| 机械性能 |
弯曲模量 |
|
ASTM 790 |
2060 |
MPa |
| Izod缺口冲击强度 |
|
ASTM D-256 |
7 |
Kg.cm/cm |
| Izod缺口冲击强度 |
|
ASTM D-256 |
1.3 |
ft.lb/in |
| 拉伸屈服强度 |
|
ASTM D-638 |
4000 |
psi |
| 弯曲模量 |
|
ASTM D-790 |
21000 |
Kg/cm2 |
| 拉伸屈服强度 |
|
ASTM D-790 |
6000 |
psi |
| 弯曲强度 |
|
ASTM D-790 |
420 |
Kg/cm2 |
| 断裂伸长率 |
|
ASTM D-638 |
80 |
% |
| 弯曲强度 |
|
ASTM D-790 |
41 |
MPa |
| 弯曲模量 |
|
ASTM D-790 |
300 |
psi |
| 拉伸屈服强度 |
|
ASTM D-638 |
280 |
Kg/cm2 |
| 拉伸屈服强度 |
|
ASTM D-638 |
28 |
MPa |
| Izod缺口冲击强度 |
|
ASTM D-256 |
70 |
J/m |
| 热性能 |
热变形温度 |
0.45Mpa |
ASTM D-648 |
138 |
℃ |
| 热变形温度 |
0.45Mpa |
ASTM D-648 |
280 |
°F |
-
-