PP | HI4352L
生产厂家：LG化学
规格用途
| 规格级别 |
高抗冲 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D-792 |
1.17 |
|
| 成型收缩率 |
|
ASTM D-955 |
0.5-0.7 |
% |
| 机械性能 |
弯曲强度 |
|
ASTM D-790 |
25 |
MPa |
| 弯曲强度 |
|
ASTM D-790 |
250 |
Kg/cm2 |
| 拉伸屈服强度 |
|
ASTM D-638 |
17 |
MPa |
| 拉伸屈服强度 |
|
ASTM D-638 |
170 |
Kg/cm2 |
| Izod缺口冲击强度 |
|
ASTM D-256 |
5.1 |
ft.lb/in |
| Izod缺口冲击强度 |
|
ASTM D-256 |
28 |
Kg.cm/cm |
| Izod缺口冲击强度 |
|
ASTM D-256 |
280 |
J/m |
| 断裂伸长率 |
|
ASTM D-638 |
60 |
% |
| 弯曲强度 |
|
ASTM D-790 |
3600 |
psi |
| 弯曲模量 |
|
ASTM D-790 |
20000 |
Kg/cm2 |
| 弯曲模量 |
|
ASTM 790 |
1960 |
MPa |
| 弯曲模量 |
|
ASTM D-790 |
280 |
psi |
| 拉伸屈服强度 |
|
ASTM D-638 |
2500 |
psi |
| 热性能 |
热变形温度 |
1.82Mpa |
ASTM D-648 |
160 |
°F |
| 热变形温度 |
0.45Mpa |
ASTM D-648 |
225 |
°F |
| 热变形温度 |
1.82Mpa |
ASTM D-648 |
70 |
℃ |
| 热变形温度 |
0.45Mpa |
ASTM D-648 |
106 |
℃ |
-
-