PP | HF3208H
生产厂家：LG化学
规格用途
| 规格级别 |
通用 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
成型收缩率 |
|
ASTM D-955 |
1.0-1.4 |
% |
| 比重 |
|
ASTM D-792 |
1.04 |
|
| 机械性能 |
弯曲强度 |
|
ASTM D-790 |
47 |
MPa |
| 弯曲模量 |
|
ASTM D-790 |
360 |
psi |
| Izod缺口冲击强度 |
|
ASTM D-256 |
40 |
J/m |
| 拉伸屈服强度 |
|
ASTM D-638 |
5000 |
psi |
| 弯曲模量 |
|
ASTM D-790 |
25000 |
Kg/cm2 |
| 断裂伸长率 |
|
ASTM D-638 |
25 |
% |
| 拉伸屈服强度 |
|
ASTM D-638 |
350 |
Kg/cm2 |
| 弯曲强度 |
|
ASTM D-790 |
480 |
Kg/cm2 |
| 弯曲强度 |
|
ASTM D-790 |
6800 |
psi |
| Izod缺口冲击强度 |
|
ASTM D-256 |
4 |
Kg.cm/cm |
| 弯曲模量 |
|
ASTM 790 |
2450 |
MPa |
| 拉伸屈服强度 |
|
ASTM D-638 |
34 |
MPa |
| Izod缺口冲击强度 |
|
ASTM D-256 |
0.7 |
ft.lb/in |
| 热性能 |
热变形温度 |
1.82Mpa |
ASTM D-648 |
195 |
°F |
| 燃烧率 |
|
ASTM UL94 |
HB |
class |
| 热变形温度 |
1.82Mpa |
ASTM D-648 |
90 |
℃ |
-
-
TOP