AS | 90HR
生产厂家：LG甬兴
规格用途
| 规格级别 |
耐热 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
流动系数 |
220℃/5kg |
ASTM D-1238 |
1.8 |
g/10min |
| 流动系数 |
220℃/10kg |
ASTM D-1238 |
18.0 |
g/10min |
| 物理性能 |
比重 |
|
ASTM D-792 |
1.07 |
|
| 变缩性 |
|
ASTM D-955 |
0.2-0.6 |
% |
| 机械性能 |
拉伸强度 |
|
ASTM D-638 |
780(76)(11200) |
kg/cm2(MPa)(Ib/in2) |
| 伸长率 |
|
ASTM D-638 |
6 |
% |
| 弯曲强度 |
|
ASTM D-790 |
1250(123)(17900) |
kg/cm2(MPa)(Ib/in2) |
| 弯曲模数 |
|
ASTM D-790 |
38500(3780)(55060) |
kg/cm2(MPa)(Ib/in2) |
| IZOD冲击强度 |
63.5×12.7×6.4mm,1/4" |
ASTM D-256 |
1.5(14.7)(0.3) |
kg.cm/cm(J/m)(Ft*Ib/in) |
| IZOD冲击强度 |
63.5×12.7×3.2mm,1/8" |
ASTM D-256 |
2.0(19.6)(0.36) |
kg.cm/cm(J/m)(Ft*Ib/in) |
| 洛氏硬度 |
|
ASTM D-785 |
122 |
R标尺 |
| 电气性能 |
HWI |
|
UL 746A |
3 |
PLC Code |
| HAI |
|
UL 746A |
0 |
PLC Code |
| HVTR |
|
UL 746A |
0 |
PLC Code |
| Arc Resistance |
|
ASTM D-495 |
5 |
PLC Code |
| CTI |
|
UL 746A |
1 |
PLC Code |
| 热性能 |
热变形温度 |
18.5kg/cm2 |
ASTM D-648 |
90 |
℃ |
| 维卡软化点 |
1000g |
ASTM D-1525 |
107 |
℃ |
| 燃烧性 |
1/8" |
UL 94 |
HB |
mm/min |
| 燃烧性 |
1/16" |
UL 94 |
HB |
mm/min |
| 燃烧性 |
1/8" |
IEC 707 |
FH3-27 |
mm/min |
-
-
TOP