PP | GP2200
生产厂家：LG化学
规格用途
| 规格级别 |
通用 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
成型收缩率 |
|
ASTM D-955 |
0.4-0.6 |
% |
| 比重 |
|
ASTM D-792 |
1.03 |
|
| 机械性能 |
Izod缺口冲击强度 |
|
ASTM D-256 |
5 |
Kg.cm/cm |
| Izod缺口冲击强度 |
|
ASTM D-256 |
0.9 |
ft.lb/in |
| Izod缺口冲击强度 |
|
ASTM D-256 |
50 |
J/m |
| 拉伸屈服强度 |
|
ASTM D-638 |
750 |
Kg./cm2 |
| 拉伸屈服强度 |
|
ASTM D-638 |
74 |
MPa |
| 弯曲模量 |
|
ASTM D-790 |
510 |
psi |
| 弯曲强度 |
|
ASTM D-790 |
98 |
MPa |
| 弯曲强度 |
|
ASTM D-790 |
14200 |
psi |
| 弯曲模量 |
|
ASTM D-790 |
36000 |
Kg./cm2 |
| 弯曲模量 |
|
ASTM 790 |
3530 |
MPa |
| 弯曲强度 |
|
ASTM D-790 |
1000 |
Kg./cm2 |
| 断裂伸长率 |
|
ASTM D-638 |
10 |
% |
| 拉伸屈服强度 |
|
ASTM D-638 |
10700 |
psi |
| 热性能 |
燃烧率 |
|
ASTM D-UL94 |
HB |
class |
| 热变形温度 |
1.82Mpa |
ASTM D-648 |
150 |
℃ |
| 热变形温度 |
1.82Mpa |
ASTM D-648 |
300 |
°F |
-
-