| 规格级别 | 透明 薄膜 均聚注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 双向拉伸薄膜挤出。适用于高速BOPP生产线。用该树脂具有优异的透明薄膜，优良的机械性能和阻隔性能。 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔体流动速率 | 190℃，2.16kg | ASTM D-1238 | 3.0 | g/10min |
| 密度 | ASTM D-792A | 0.9 | g/cm3 | ||
| 机械性能 | 屈服拉伸强度 | ASTM D-638 | 32 | MPa | |
| 屈服伸长率 | ASTM D-638 | 9 | % | ||
| 断裂拉伸强度 | ASTM D-638 | 19 | MPa | ||
| 断裂伸长率 | ASTM D-638 | 165 | % | ||
| 弯曲模量 | ASTM D-790 | 1265 | MPa | ||
| 弯曲强度 | ASTM D-790 | 35 | MPa | ||
| 悬臂梁冲击强度，缺口 | 23deg C | ASTM D-256 | 2.8 | kJ/m2 | |
| 洛氏硬度 | ASTM D-785 | 98 | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 100 | MPa | |
| 断裂拉伸强度 | TD | ASTM D-882 | 215 | g | |
| 断裂伸长率 | MD | ASTM D-882 | 85 | % | |
| 断裂伸长率 | TD | ASTM D-882 | 15 | % | |
| 1%割线模量 | MD | ASTM D-882 | 2100 | MPa | |
| 1%割线模量 | TD | ASTM D-882 | 3850 | MPa | |
| 光学性能 | 雾度 | ASTM D-1003 | 0.1 | % | |
| 光泽度 | 45度 | ASTM D-2457 | 155 | ||
| 热性能 | 维卡软化温度 | 10N | ASTM D-1525 | 153 | ℃ |