ABS | 700
生产厂家：日本东丽
规格用途
| 规格级别 |
通用 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
熔体流动速率 |
220℃ 10kg |
ISO-1133 |
23 |
g/10min |
| 比重 |
23℃ |
ASTM D-792 |
1.05 |
|
| 模塑收缩率 |
|
ASTM D-955 |
0.4-0.6 |
% |
| 体积阻力 |
23℃ |
ASTM D-257 |
＞1016 |
ohm.cm |
| 阻燃性 |
|
UL-94 |
HB |
|
| 吸水性 |
23℃×24hrs |
ASTM D-570 |
0.3 |
% |
| 表面阻力 |
23℃ |
ASTM D-257 |
＞1016 |
ohm |
| 机械性能 |
拉伸断裂伸长率 |
23℃ |
ASTM D-638 |
35 |
% |
| 弯曲模量 |
23℃ |
ASTM D-790 |
25000(2450) |
kg/cm2(MPa) |
| IZOD冲击强度 |
12.7×62.5×12.7mm |
0℃ |
ASTM D-256 |
11(108) |
kg.cm/cm(J/m) |
| 12.7×62.5×3.2mm |
0℃ |
ASTM D-256 |
16(157) |
kg.cm/cm(J/m) |
| IZOD冲击强度 |
12.7×62.5×12.7mm |
23℃ |
ASTM D-256 |
19(186) |
kg.cm/cm(J/m) |
| 12.7×62.5×3.2mm |
23℃ |
ASTM D-256 |
20(196) |
kg.cm/cm(J/m) |
| 洛氏硬度 |
|
ASTM D-785 |
115 |
R |
| 弯曲强度 |
23℃(strainrate:3%) |
ASTM D-790 |
770(76) |
kg/cm2(MPa) |
| IZOD冲击强度 |
12.7×62.5×12.7mm |
-30℃ |
ASTM D-256 |
8(78) |
kg.cm/cm(J/m) |
| 12.7×62.5×3.2mm |
-30℃ |
ASTM D-256 |
12(118) |
kg.cm/cm(J/m) |
| 拉伸强度 |
23℃(strainrate:5%) |
ASTM D-638 |
510(50) |
kg/cm2(MPa) |
| 电气性能 |
绝缘强度 |
Short time |
ASTM D-194 |
23 |
KV/mm |
| 电力因数 |
1000Hz |
ASTM D-150 |
6.1×10-3 |
|
| 介电常数 |
1000Hz |
ASTM D-150 |
3.1 |
|
| 热性能 |
热传导性能 |
|
ASTM C177 |
0.15 |
W/K.m |
| 线性膨胀系数 |
|
ASTM D-696 |
7.1×10-5 |
mm/mm℃ |
| 热变形温度 |
127×12.7×12.7mm |
18.56kg/cm2 |
ASTM D-648 |
92 |
℃ |
| 127×12.7×6.4mm |
18.56kg/cm2 |
ASTM D-648 |
87 |
℃ |
-
-